HiFlexTM CIIR is a blended chlorinated co-polymer of isobutylene and isoprene. HiFlexTM CIIR has very good processability and is compatible for co-curing with conventional diene rubbers. It shows good resistance to oxidation and ozone degradation and has low gas permeability.
Applications:
Tyre innerliners, hoses, seals, and membranes etc.
Supply Form:
34 kgs bale wrapped in dispersible film.
RAW MATERIAL PROPERTIES
| Properties | Nominal Value | Test Method |
| Mooney Viscosity (ML 1+8@125℃) | 38 +/- 5 MU | ASTM D1646 |
| Chlorine Content | 0.9% min | Internal Method |
| Moisture Content | 1.0% max | Internal Method |
| Ash Content | 1.0% max | ASTM D297-35 |
| Density | 0.92 g/cm³ | ISO 1183 |
| Antioxidant | Non-Staining | – |
| Physical Properties* | Value |
| Tensile Strength | 13.2 MPa |
| Modulus at 100% EB | 5.4 MPa |
| Elongation at Break | 430% |
| Hardness | 60 Shore A |
* Characteristics determined on a HEPL compound of the following formulation. Press Cure: 20 mins @ 160℃
| HiFlexTM CIIR | 100 |
| HAF N-330 | 40 |
| Zinc Oxide | 5 |
| Stearic Acid | 1 |
| Qureacc® MBTS | 1 |
| Sulfur | 1.5 |