HiFlexTM EP-201 ( Non Oil )
HiFlexTM EP-201 is a blended terpolymer of ethylene, propylene and diene. HiFlexTM EP-201 has very good processability and is compatible for co-curing with conventional diene rubbers. It shows excellent resistance to oxidation and ozone degradation.
Applications:
Automotive and window profiles, grommets, pipe seals, sheets, and other industrial products requiring ozone resistance.
Supply Form:
34 kgs bale wrapped in dispersible film.
RAW MATERIAL PROPERTIES
| Properties | Nominal Value | Test Method |
|---|---|---|
| Mooney Viscosity (ML 1+4@1250 C) | 60 +/- 10 MU | ASTM D1646 |
| Ethylene Content | 63 +/- 5% | Internal Method |
| ENB Content | 5 +/- 1% | Internal Method |
| Moisture Content | 1.0% max | Internal Method |
| Ash Content | 1.5% max | ASTM D297-35 |
| Density | 0.86 g/cm 3 | ISO 1183 |
| Antioxidant | Non-Staining | – |
| Physical Properties* | Value |
|---|---|
| Tensile Strength | 14.2 MPa |
| Modulus at 100% EB | 4.3 MPa |
| Elongation at Break | 400% |
| Hardness | 65 Shore A |
*Characteristics determined on a HEPL compound of the following formulation. Press Cure: 10 mins @ 1600C
| HiFlexTM EP-201 | 100 |
|---|---|
| Zinc Oxide | 5 |
| Stearic Acid | 1 |
| FEF N-550 | 80 |
| Paraffinic Oil | 20 |
| Qureacc® TMT | 0.5 |
| Qureacc® MBT | 0.5 |
| Qureacc® ZDBC | 1 |
| Qureacc® MBTS | 1 |
| Sulfur | 1.7 |